Описание материалов:
Andur 95-AP is a polyether (PTMG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 95 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442 and other diamines, and by the use of plasticizers.
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.14 | g/cm³ | ASTM D1505 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 95 | | ASTM D2240 |
| Shaw D | 47 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 15.0 | MPa | ASTM D412 |
| 300% strain | 29.8 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 52.4 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 370 | % | ASTM D412 |
| Комплект сжатия | 28 | % | ASTM D395B |
| Сопротивляемость Bayshore | 45 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 3.0 - 5.0 | min | |
| Время демолд (100°C) | 20 - 25 | min | |
| Время доставки (100°C) | 3.0 | hr | |
| Дополнительная информация |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 93 to 97Durometer Hardness, ASTM D2240, Shore D: 46 to 48Die C Tear, ASTM D1004: 600 pliAverage Split Tear, ASTM D1938: 150 pliStoichiometry Curative Level: 95%Cure Time, 150 to 160°F: OvernightMix Temperature:
Andur 95 AP: 180-212°F
Curene 442: 250°F |