TOTAL Polyethylene HDPE 6410
| Категория | HDPE, High Density (MMW) Polyethylene , HDPE, MMW |
| Производитель | TOTAL Refining & Chemicals |
| Торговая марка | TOTAL Polyethylene |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
4xP2QR_TOTAL-Polyethylene-HDPE-6410.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
TOTAL Polyethylene 6410 is a high density (MMW) polyethylene material,. This product is available in North America or Asia Pacific region. The processing method is: film extrusion or co-extrusion molding.
The main features of TOTAL Polyethylene 6410 are:
Typical application areas include:
The main features of TOTAL Polyethylene 6410 are:
- Comply with REACH standard
- High stiffness
- Good processability
- Transparency
Typical application areas include:
- bag/lining
- Movie
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.961 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 1.2 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 33 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сектантный модуль 1 | ASTM D882A | ||
| 1% secant, MD : 25 µm, blown film | 862 | MPa | ASTM D882A |
| 2% secant, MD : 25 µm, blown film | 689 | MPa | ASTM D882A |
| 1% secant, TD : 25 µm, blown film | 883 | MPa | ASTM D882A |
| 2% secant, TD : 25 µm, blown film | 703 | MPa | ASTM D882A |
| Прочность на растяжение 2 | ASTM D882A | ||
| MD : Yield, 25 µm, blown film | 26.2 | MPa | ASTM D882A |
| TD : Yield, 25 µm, blown film | 27.6 | MPa | ASTM D882A |
| MD : Broken, 25 µm, blown film | 51.7 | MPa | ASTM D882A |
| TD : Broken, 25 µm, blown film | 23.4 | MPa | ASTM D882A |
| Удлинение при растяжении 3 | ASTM D882A | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| TD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 24 | g | ASTM D1922 |
| TD : 25 µm, blown film | 390 | g | ASTM D1922 |
| Скорость передачи водяного пара (38°C, 25 µm, Blown Film) | 6.2 | g/m²/24 hr | ASTM F1249 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Пиковая температура плавления | 134 | °C | ASTM D3418 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блестящий Гарднер (25.4 µm, Blown Film) | 50 | ASTM D523 | |
| Haze (25.4 µm, Blown Film) | 15 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| WVTR, ASTM E96, 100°F, Blown Film, 1 mil: 0.4 g/100in²/day |
| Примечание | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Тип материала | Категория | Производитель |
|---|---|---|
| TOTAL Polyethylene HDPE XS 10 OS | HDPE | TOTAL Refining & Chemicals |
| AZR-Ecoplast 143 HDPE red 0.4 | HDPE | UrbanPlast SIA |
| CERTENE™ HWF-849A | HDPE | Muehlstein |
| CONTINUUM™ DMDC-1250 NT 7 | HDPE | The Dow Chemical Company |
| Eltex® B4922/50N3000 | HDPE | INEOS Olefins & Polymers Europe |
| Eraclene® FC 82 | HDPE | Versalis S.p.A. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved