TOTAL Polyethylene Lumicene® M 3410 EP (EU)
Описание материалов:
Lumicene® mPE M 3410 EP is a second generation metallocene based Medium Density Polyethylene with hexene as comonomer.
Lumicene® mPE M 3410 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential.
Lumicene® mPE M 3410 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE.
Lumicene® mPE M 3410 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, mailing film, heavy-duty sacks, bags, lamination and hygiene film.
| Главная Информация | |
|---|
| Добавка | - Антиоксидант
- Обработка помощи
|
| Характеристики | - Хорошее тепловое уплотнение
- Хорошая прочность на разрыв
- Термогерметичный
- Гексен-комномер
- Высокая четкость
- Глянцевый
- Высокая жесткость
- Стойкий к проколу
|
| Используется | - Сумки
- Смешивание
- Потребительские приложения
- Пленка
- Пищевая упаковка
- Сверхпрочные сумки
- Ламинаты
- Многослойная пленка
- Упаковка
- Термоусадочная пленка
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | - Выдувная пленка
- Коэкструзия
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.934 | g/cm³ | ASTM D792, ISO 1183 |
| Массовый расход расплава (MFR) | | | |
| 190°C/2.16 kg | 0.90 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/21.6 kg | 30 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (vs. Itself - Static, Blown Film) | 0.40 | | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 to 41 | µm | |
| Сектантный модуль | | | ASTM D882A |
| 1% Secant, MD
: Blown Film | 365 | MPa | |
| 1% Secant, TD
: 25 µm, Blown Film | 386 | MPa | |
| Tensile Stress | | | |
| MD
: Yield, 40 µm, Blown Film | 17.0 | MPa | ISO 527-3 |
| TD
: Yield, 40 µm, Blown Film | 18.0 | MPa | ISO 527-3 |
| MD
: Break, 25 µm, Blown Film | 44.1 | MPa | ASTM D882A |
| TD
: Break, 25 µm, Blown Film | 42.1 | MPa | ASTM D882A |
| MD
: Break, 40 µm, Blown Film | 47.0 | MPa | ISO 527-3 |
| TD
: Break, 40 µm, Blown Film | 43.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | |
| MD
: Break, 25 µm, Blown Film | 400 | % | ASTM D882A |
| TD
: Break, 25 µm, Blown Film | 650 | % | ASTM D882A |
| MD
: Break, 40 µm, Blown Film | 630 | % | ISO 527-3 |
| TD
: Break, 40 µm, Blown Film | 700 | % | ISO 527-3 |
| Ударное падение Dart | | | |
| 25 µm, Blown Film | 60 | g | ASTM D1709A |
| 40 µm, Blown Film | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 25 µm, Blown Film | 55 | g | |
| TD
: 25 µm, Blown Film | 400 | g | |
| Температура инициализации уплотнения | 120 | °C | |
| Передача водяного пара | 10 | g/m²/24 hr | ASTM E96 |
| Elmendorf Tear Strength 1 | | | ISO 6383-2 |
| MD
: 40.0 µm | 20.0 | kN/m | |
| TD
: 40.0 µm | 100.0 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 123 | °C | ISO 306 |
| Температура плавления | 124 | °C | ISO 11357-3, ASTM D3417 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блестящий Гарднер (45°, 25.4 µm, Blown Film) | 65 | | ASTM D523 |
| Блеск (45°, 40.0 µm, Blown Film) | 60 | | ASTM D2457 |
| Haze | | | |
| 25.4 µm, Blown Film | 9.0 | % | ASTM D1003 |
| 40.0 µm, Blown Film | 9.0 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 200 | °C | |