DOWLEX™ 2107B
| Категория | LLDPE, Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOWLEX™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
4b5VLT_DOWLEX-2107B.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOWLEX™ 2107B Polyethylene Resin with Extra Stretch Performance is an Ethylene-1-Octene copolymer designed for cast film applications, such as industrial pallet wrap. DOWLEX 2107B provides stretch film with superior extensibility and increased resistance to failure around film flaws while maintaining exceptional puncture resistance and load retention.
Main Characteristics:
Complies with:
Suitable for food contact, Report # 927/09 issued by INAL according to MERCOSUR.
Main Characteristics:
- Industrial stretch film
- Film for products for adult incontinence
- Film for products for femine hygiene
Complies with:
- U.S. FDA 21 CFR 177.1520 (c) 3.2a
- EU, No 10/2011
Suitable for food contact, Report # 927/09 issued by INAL according to MERCOSUR.
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.6 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сопротивление проколу пленки (22 µm) | 157 | J/cm³ | Internal method |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 22 µm | 189 | MPa | ASTM D882 |
| 2% secant, TD : 22 µm | 196 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 22 µm | 10.9 | MPa | ASTM D882 |
| TD : Yield, 22 µm | 10.8 | MPa | ASTM D882 |
| MD : Break, 22 µm | 30.3 | MPa | ASTM D882 |
| TD : Break, 22 µm | 28.5 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 590 | % | ASTM D882 |
| TD : Fracture | 870 | % | ASTM D882 |
| Ударное падение Dart (22 µm) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 22 µm | 160 | g | ASTM D1922 |
| TD : 22 µm | 710 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 22.0 µm) | 78 | ASTM D2457 | |
| Haze (22.0 µm) | 5.2 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| 22 um 薄膜挤出铸造的推荐加工条件： 熔体温度：220 - 280C 冷却辊温度：15 - 60C 生产线速度：150 - 600 米/分 厚度：10 - 60 微米 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Comai 663-3 BA | LLDPE | Comai Ltda |
| DOW™ LLDPE DNDA-7144 NT 7 | LLDPE | The Dow Chemical Company |
| ASPUN™ 6835A | LLDPE | The Dow Chemical Company |
| DOWLEX™ NG 2045.11B | LLDPE | The Dow Chemical Company |
| Hypel® PELLD5/.935 | LLDPE | Entec Polymers |
| ICORENE® N2303 | LLDPE | ICO Polymers EMEA, A Division of A. Schulman |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved