Описание материалов:
Vydyne 47H BK0501 is general-purpose, impact-modified PA66 resin. Available in black, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 47H BK0501 was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated.
Vydyne 47H BK0501 is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 47H BK0501 is designed to meet the critical low-temperature impact requirements called out in many automotive specifications.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Сопротивление бензину
- Общее назначение
- Хорошая стойкость к истиранию
- Хорошая химическая стойкость
- Хорошая технологичность
- Хорошая прочность
- Высокая ударопрочность
- Модификация удара
- Ударопрочность при низкой температуре
- Прочность при низкой температуре
- Маслостойкий
- Устойчивость к растворителям
|
| Используется | - Автомобильные Приложения
- Разъемы
- Потребительские приложения
- Электрическое/электронное применение
- Крепежные детали
- Шестерни
- Промышленное применение
|
| Рейтинг агентства | - Астм д 4066 PA0161
- Астм д 6779 PA0161
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Плотность | 1.10 | -- | g/cm³ | ISO 1183 |
| Формовочная усадка | | | | ISO 294-4 |
| Across Flow
: 2.00 mm | 1.6 | -- | % | |
| Flow
: 2.00 mm | 1.8 | -- | % | |
| Поглощение воды | | | | ISO 62 |
| 23°C, 24 hr | 1.2 | -- | % | |
| Equilibrium, 50% RH | 2.3 | -- | % | |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2780 | 1740 | MPa | ISO 527-2 |
| Tensile Stress | | | | ISO 527-2 |
| Yield | 60.0 | 45.0 | MPa | |
| Break | 52.0 | 40.0 | MPa | |
| Растяжимое напряжение (Break) | 22 | 60 | % | ISO 527-2 |
| Флекторный модуль | 2300 | 780 | MPa | ISO 178 |
| Флекторный стресс | 70.0 | 24.0 | MPa | ISO 178 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179 |
| -40°C | 11 | 18 | kJ/m² | |
| -30°C | 17 | 24 | kJ/m² | |
| 23°C | 19 | 62 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | | ISO 179 |
| -30°C | No Break | No Break | | |
| 23°C | No Break | No Break | | |
| Зубчатый изод ударная прочность | | | | ISO 180 |
| -40°C | 12 | 18 | kJ/m² | |
| -30°C | 16 | 24 | kJ/m² | |
| 23°C | 18 | 44 | kJ/m² | |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 185 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 63.0 | -- | °C | ISO 75-2/A |
| Температура плавления | 260 | -- | °C | ISO 11357-3 |
| CLTE | | | | ISO 11359-2 |
| Flow
: 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C | |
| Transverse
: 23 to 55°C, 2.00 mm | 1.4E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.750 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI Str | | | | UL 746 |
| 0.750 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 115 | -- | °C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости (0.750 mm) | 1.0E+11 | -- | ohms·cm | IEC 60093 |
| Диэлектрическая прочность (1.00 mm) | 12 | -- | kV/mm | IEC 60243 |
| Дуговое сопротивление | PLC 6 | -- | | ASTM D495 |
| Comparative Tracking Index (3.00 mm) | 525 | -- | V | IEC 60112 |
| Высокоусиленное дуговое зажигание (HAI) | | | | UL 746 |
| 0.750 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| Высоковольтная скорость отслеживания дуги (HVTR) | PLC 2 | -- | | UL 746 |
| Зажигание горячей проволоки (HWI) | | | | UL 746 |
| 0.750 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 4 | -- | | |
| 3.00 mm | PLC 3 | -- | | |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| Индекс воспламеняемости провода свечения | | | | IEC 60695-2-12 |
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 775 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Температура зажигания провода свечения | | | | IEC 60695-2-13 |
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 800 | -- | °C | |
| 3.00 mm | 725 | -- | °C | |
| Дополнительная информация | Сухой | Состояние | | Метод испытания |
|---|
| Automotive Materials -
(thickness d = 1 mm) | + | -- | | FMVSS 302 |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемый Макс измельчения | 25 | % | |
| Задняя температура | 280 to 310 | °C | |
| Средняя температура | 280 to 310 | °C | |
| Передняя температура | 280 to 310 | °C | |
| Температура сопла | 280 to 310 | °C | |
| Температура обработки (расплава) | 285 to 305 | °C | |
| Температура формы | 65.0 to 95.0 | °C | |