Escorene™ Ultra FL 00728CC
Описание материалов:
FL 00728CC is a good co-extrusion component in extrusion coating, blown film and casting film. It can be well bonded to stretched polypropylene in co-extrusion. This brand has good optical properties, low crystal point and extremely low sealing temperature when used for heat sealing. Good extrusion coating effect can be obtained at 200°C (392 °F) under processing conditions. Processing temperatures above 220°C (428 °F) may cause resin degradation. FL00728CC should be put into the extruder after low density polyethylene with similar or higher melt index. The machine should be thoroughly cleaned with low density polyethylene or suitable detergent before stopping.
| Главная Информация | |
|---|
| Добавка | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Содержание винилацетата | 27.5 | wt% | ExxonMobil Method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A, 15 sec) | 80 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения 1 | 17.0 | MPa | ASTM D638 |
| Удлинение при растяжении 2(Break) | > 100 | % | ASTM D638 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 43.0 | °C | ASTM D1525 |
| Юридическое заявление |
|---|
| 本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。 |
| Инструкции по экструзии |
|---|
| Excellent results are obtained in extrusion coating at 200°C (392°F) temperature range. Processing temperatures above 220°C (428°F) may cause resin degradation. FL00728CC should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown. |
| Примечание |
|---|
| 1 . | 5.0 mm/min |
| 2 . | 500 mm/min |