Описание материалов:

LUVOCOM®1800-7432 is a polyethylene terephthalate (PET) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1800-7432 are:

Wear-resistant

Lubrication

Typical application areas include:

textile/fiber

engineering/industrial accessories

Automotive Industry

business/office supplies

Главная Информация
Добавка	Ptfe лубрикант
Характеристики	Низкий коэффициент трения Хорошая стойкость к истиранию Смазка
Используется	Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование
Внешний вид	Белый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.41	g/cm³	ISO 1183
Формовочная усадка	1.6 - 2.2	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	3000	MPa	ISO 527-2
Tensile Stress (Break)	60.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	3.0	%	ISO 527-2

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	40	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	100	°C	UL 746B
Максимальная рабочая температура- Короткий срок	180	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167
Удельное сопротивление поверхности	> 1.0E+12	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
B	80.0	°C
Hot air dryer, A	120	°C
Время сушки
B	6.0 - 8.0	hr
Hot air dryer, A	2.0 - 5.0	hr
Рекомендуемая максимальная влажность	0.020	%
Задняя температура	285 - 295	°C
Средняя температура	270 - 280	°C
Передняя температура	265 - 275	°C
Температура сопла	265 - 275	°C
Температура обработки (расплава)	280	°C
Температура формы	60.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 300°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 300°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
DSR TL-8080	PET	Dragon Special Resin (Xiamen) Co., Ltd.
Skyrol® SH94	PET	SKC Inc.
Skyrol® SH64	PET	SKC Inc.
RTP 1108 BLK	PET	RTP Company
Mylar® EL (92 guage)	PET	DuPont Teijin Films U.S.