Andur 8-5 APLF/Curene® 442
Описание материалов:
Andur 8-5 APLF is a polyester based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 84 to 86 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442, other diamines or through the use of plasticizers.
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.25 | g/cm³ | ASTM D1505 |
| Формовочная усадка-
Поток | 1.3 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 85 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 5.34 | MPa | ASTM D412 |
| 300% strain | 8.79 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 46.2 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 650 | % | ASTM D412 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 5.5 - 6.0 | min | |
| Время демолд (100°C) | 30 | min | |
| Время доставки (100°C) | 16 | hr | |
| Дополнительная информация |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 84 to 86Die C Tear, ASTM D1004: 475 pliAverage Split Tear, ASTM D1938: 300 pliStoichiometry Curative Level: 95%Mix Temperature:
Andur 8-5 APLF: 160-180°F
Curene 442: 230-240°F |