Описание материалов:
Telcar TELC-340 is a general purpose thermoplastic elastomer designed for the consumer and industrial markets. Telcar TELC-340 is a high hardness, low density grade that is suitable for extrusion and injection molding.
| Главная Информация | |
|---|
| Характеристики | |
| Используется | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.888 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра 1(Shore A, 5 sec) | 94 | | ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Флекторный модуль | 172 | MPa | ASTM D790 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ISO 37 |
| Transverse flow
: 100% strain | 6.24 | MPa | ISO 37 |
| Flow
: 100% strain | 8.31 | MPa | ISO 37 |
| Прочность на растяжение | | | ISO 37 |
| Transverse flow
: Fracture | 12.5 | MPa | ISO 37 |
| Flow
: Fracture | 9.90 | MPa | ISO 37 |
| Удлинение при растяжении | | | ISO 37 |
| Transverse flow
: Fracture | 810 | % | ISO 37 |
| Flow
: Fracture | 560 | % | ISO 37 |
| Прочность на разрыв-
Поперечный поток | 74.0 | kN/m | ISO 34 |
| Комплект сжатия 2(23°C, 22 hr) | 57 | % | ISO 815 |
| Старение | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Изменение прочности на растяжение в воздухе | | | ISO 188 |
| 110°C, 1008 hr | -7.2 | % | ISO 188 |
| 125°C, 168 hr | -4.0 | % | ISO 188 |
| Изменения напряжения при растяжении при переломе воздуха-
Поперечный поток | | | ISO 188 |
| 110°C, 1008 hr | -14 | % | ISO 188 |
| 125°C, 168 hr | -8.3 | % | ISO 188 |
| Изменение твердости по суше в воздухе | | | ISO 188 |
| Support a, 110°C, 1008 hr | -0.20 | | ISO 188 |
| Support a, 125°C, 168 hr | 0.50 | | ISO 188 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -50.0 | °C | ASTM D746 |
| Анализ заполнения | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Видимая вязкость (200°C, 206 sec^-1) | 322 | Pa·s | ASTM D3835 |
| Юридическое заявление |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Задняя температура | 171 - 193 | °C | |
| Средняя температура | 177 - 199 | °C | |
| Передняя температура | 182 - 204 | °C | |
| Температура сопла | 188 - 210 | °C | |
| Температура обработки (расплава) | 188 - 210 | °C | |
| Температура формы | 25.0 - 65.6 | °C | |
| Давление впрыска | 1.38 - 6.89 | MPa | |
| Скорость впрыска | Moderate-Fast | | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Подушка | 3.81 - 25.4 | mm | |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 166 - 188 | °C | |
| Зона цилиндра 2 температура. | 171 - 193 | °C | |
| Зона цилиндра 3 темп. | 177 - 199 | °C | |
| Зона цилиндра 5 темп. | 182 - 204 | °C | |
| Температура матрицы | 190 - 210 | °C | |
| Инструкции по экструзии |
|---|
| Screw Speed: 30 to 100 rpm |
| Примечание |
|---|
| 1 . | Instant |
| 2 . | Method A |