Описание материалов:
HWF-0150 is a certified prime grade Hexene copolymer HIGH MOLECULAR WEIGHT developed for blown films. HWF-0150 can be used alone or in BLENDS with HMW-HDPE and/or LLDPE Blown film grades. HWF-0150 features UNIMODAL molecular weight distribution for improved processability at lower extruder pressure and good film stiffness. HWF-0150 can be used in a broad range of applications blended from 10% to 50% with either HMW-HDPE and/or LLDPE. HWF-0150 can be processed on HMW, high stalk film equipment with a die gap >0.75 to 1.25< mm.. HMF-0150 applications include industrial and trash can liners, as well as T-shirt bags. Recommended processing temperatures 195 to 205°C. HWF-0150 complies with FDR regulation 21CFR 177.1520 (c) 3.1 (a) + 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, хороший
- Сополимер
- Гексен-комномер
- Обрабатываемость, хорошая
- Соответствие пищевого контакта
|
| Используется | - Пленка
- Подкладка
- Сумка
- Промышленное применение
- Смешивание
- Тяжелая упаковочная сумка
|
| Рейтинг агентства | - FDA 21 CFR 177,1520 (c) 3.1a
- FDA 21 CFR 177,1520 (c) 3.2a
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.950 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | < 0.10 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 12 | µm | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 12 µm | 26.0 | MPa | ASTM D882 |
| TD
: Yield, 12 µm | 14.0 | MPa | ASTM D882 |
| MD
: Break, 12 µm | 61.0 | MPa | ASTM D882 |
| TD
: Break, 12 µm | 27.0 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break, 12 µm | 300 | % | ASTM D882 |
| TD
: Break, 12 µm | 410 | % | ASTM D882 |
| Ударное падение Dart 1(12 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 12 µm | 15 | g | ASTM D1922 |
| TD
: 12 µm | 25 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура плавления | 130 | °C | ASTM D3417 |
| Дополнительная информация |
|---|
| Film Specimen: 0.5 mil (12 µm) film, melt temperature 410-440°F (210-225°C), blow-up-ratio 4.0:1, frost line height 5 x die ø. |