Описание материалов:
A Skived PTFE film that is produced from a modified homopolymer PTFE resin containing <1% of a fully fluorinated comonomer. The incorporation of the comonomer yields a material with improved electrical and physical properties. This film can be thermally fused to itself. The modified homopolymer resin exhibits chemical resistance equivalent to that of a standard homopolymer PTFE. It's tensile strength is approximately 10% higher and the elongation is approximately 30% higher than for a standard homopolymer PTFE.
With its ability to be heat fused, this film finds applications in the convoluted PTFE hose industry as a inner liner material.
| Главная Информация | |
|---|
| Характеристики | - Хорошая химическая стойкость
- Хорошие электрические свойства
- Высокое удлинение
- Высокая прочность на растяжение
- Гомополимер
|
| Используется | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | |
|---|
| Толщина | 25.4 to 1020 | nm | |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|
| Идентификатор ядра | 7.62 | cm | |
| Максимальный диаметр рулона | 356 | mm | |
| Ширина | 6.35 to 1140 | mm | |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение-
MD (Yield) | 24.8 | MPa | ASTM D882 |
| Растяжимое удлинение-
MD (Break) | 250 | % | ASTM D882 |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Температура непрерывного использования | 260 | °C | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Диэлектрическая прочность | 98 | kV/mm | ASTM D149 |