Bexloy® W

Категория	Ionomer
Производитель	DuPont Packaging & Industrial Polymers
Торговая марка	Bexloy®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	2Ef3Tf_Bexloy-W.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Bexloy® W is available in a variety of grades. The properties below represent the range of properties for most grades. Where only one number is listed, all grades are represented by that value.
Bexloy® W modified ionomer resins were first engineered for injection molded exterior automotive applications such as molded-in-color fascia, bumper covers, side moldings and other decorative trim.

Главная Информация
Характеристики	Подсветка Сопротивление пятнам Перерабатываемые материалы Хорошая стабильность цвета Хорошая окраска Хорошая стойкость к истиранию Ударопрочность при низкой температуре Устойчивость к царапинам Хорошая стойкость к истиранию Хорошая устойчивость к погоде
Используется	Применение в автомобильной области Автомобильные внутренние детали Автомобильные внешние части
Внешний вид	Черный Натуральный цвет
Формы	Частицы
Метод обработки	Литье под давлением

Физический	Номинальное значение	Единица измерения	Метод испытания
Удельный вес	0.963	g/cm³	ASTM D792
Формовочная усадка- Поток	0.98	%	ASTM D955

Механические	Номинальное значение	Единица измерения	Метод испытания
Прочность на растяжение (23°C)	20.7	MPa	ASTM D638
Удлинение при растяжении (Break, 23°C)	400	%	ASTM D638
Флекторный модуль- Касательная (23°C)	707	MPa	ASTM D790

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Зубчатый изод Impact (23°C)	850	J/m	ASTM D256
Ударное падение Dart (-30°C)	36.2	J	ASTM D3029

Тепловой	Номинальное значение	Единица измерения	Метод испытания
CLTE- Поток (-30 to 80°C)	8.3E-5	cm/cm/°C	ASTM D696

Дополнительная информация
The value listed as CLTE, ASTM 696, was tested in accordance with ASTM E831.Heat Sag, ASTM D3769, 152mm (6 in) Overhang, 30min, @ 180°F: 0.5inTear Resistance, ASTM D624, Die C, 508mm (20in)/min, @ 73°F: 850 to 970lb/inGardner Impact, ASTM D3209, -22°F: >320 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, 73°F: 194 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, -22°F: 159 in-lb3Elongation at Break, ASTM D638, 73°F: >400%Flexural Modulus, Tangent, 73°F, ASTM D790: 95 to 110 kpsiSpecific Gravity, 73°F, ASTM D792: 0.96 to 0.97Tensile Strength, 73°F, ASTM D638: 2800 to 3200 psiShrinkage, ASTM D955: 0.75 to 1.2%Coefficient of Linear Thermal Expansion, -22 to 176°F, ASTM E831: 4.2 to 5.0 x 10^-5

Дополнительная информация

The value listed as CLTE, ASTM 696, was tested in accordance with ASTM E831.Heat Sag, ASTM D3769, 152mm (6 in) Overhang, 30min, @ 180°F: 0.5inTear Resistance, ASTM D624, Die C, 508mm (20in)/min, @ 73°F: 850 to 970lb/inGardner Impact, ASTM D3209, -22°F: >320 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, 73°F: 194 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, -22°F: 159 in-lb3Elongation at Break, ASTM D638, 73°F: >400%Flexural Modulus, Tangent, 73°F, ASTM D790: 95 to 110 kpsiSpecific Gravity, 73°F, ASTM D792: 0.96 to 0.97Tensile Strength, 73°F, ASTM D638: 2800 to 3200 psiShrinkage, ASTM D955: 0.75 to 1.2%Coefficient of Linear Thermal Expansion, -22 to 176°F, ASTM E831: 4.2 to 5.0 x 10^-5

Тип материала	Категория	Производитель
TECHNOGRAN® IONOMERE NAT CLEAR	Ionomer	Eurocompound Polymers
CLARIX® 110901-01 Clear	Ionomer	A. Schulman Inc.
Surlyn® E185SB	Ionomer	DuPont Packaging & Industrial Polymers
Surlyn® 2601	Ionomer	DuPont Packaging & Industrial Polymers
Surlyn® 1652SB	Ionomer	DuPont Packaging & Industrial Polymers
AMPLIFY™ IO 3801	Ionomer	The Dow Chemical Company

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

