Описание материалов:
EZ~Spray® Silicone 20 is a sprayable silicone that cures quickly to a soft rubber with high elongation and tear strength. Liquid silicone is sprayed through the EZ~Spray® Junior Cartridge System which is an economical alternative to expensive spray equipment. After a suitable spray thickness is attained, EZ~Spray® Silicone 20 cures in about 10 minutes with negligible shrinkage to a strong, durable mold rubber good for production casting of polyester, epoxy or urethane resins, gypsum, concrete and other materials.
EZ~Spray® Silicone 20 is effective at making fast, cost effective vacuum bags for producing composite parts. Newly sprayed or injected bags can be removed from the mold in 10 minutes and used immediately in production with polyester or epoxy resin systems. The advantage that EZ~Spray® Silicone 20 offers vs. conventional vacuum bagging systems is the speed at which a production-ready silicone bags can be made resulting in significant time and labor savings. Read the EZ~Spray® Junior manual prior to spraying.
| Главная Информация | |
|---|
| Характеристики | - Прочный
- Хорошая прочность
- Хорошая прочность на разрыв
- Высокое удлинение
- Низкая усадка
|
| Используется | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.08 | g/cm³ | ASTM D1475 |
| Удельный объем | 0.925 | cm³/g | ASTM D1475 |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Service Temperature | -54 to 232 | °C | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Cure Time | 20.0 | min | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Формовочная усадка-
Поток | < 0.10 | % | ASTM D2566 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 20 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress (100% Strain) | 0.317 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 3.79 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 620 | % | ASTM D412 |
| Tear Strength 1 | 21.0 | kN/m | ASTM D624 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта | | | |
| Part A | Mix Ratio by Weight: 1.0 | | |
| Part B | Mix Ratio by Weight: 1.0 | | |
| Срок службы горшка (23°C) | 3.0 | min | ASTM D2471 |
| Терморегулирующая вязкость | 20000 | cP | ASTM D2393 |