Описание материалов:
Asahi Kasei Tuftec™ Trial L521 is particularly designed as a modifier to increase flexibility of polypropylene (PP). Its excellent compatibility makes L521 super-finely dispersed into PP. PP and L521 blends provides transparent and flexible extruded products such as sheets, films and tubes. The blends are also applicable to injection molding due to its high MFR. It has excellent adhesion, which is suitable for the use of adhesive layer of protective films with hot-melt and pressure sensitive characteristics. L521 meets USP Class VI standards. It may be used for medical applications after a special agreement with Asahi Kasei.
| Главная Информация | |
|---|
| Характеристики | |
| Используется | - Пленка
- Фитинги для труб
- Лист
- Пластиковая модификация
- Медицинские принадлежности/принадлежности для ухода
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.890 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) | | | ISO 1133 |
| 190°C/2.16 kg | 2.3 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 15 | g/10 min | ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 39 | | ISO 7619 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress (300% Strain) | 1.30 | MPa | ISO 37 |
| Tensile Stress 1(Break) | 12.5 | MPa | ISO 37 |
| Удлинение при растяжении 2(Break) | 810 | % | ISO 37 |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Styrene/Rubber ratio | 18/82 | | Internal method |
| Примечание |
|---|
| 1 . | Type 1A, 500mm/min |
| 2 . | Type 1A, 500mm/min |