Описание материалов:
TECANAT is a natural unfilled polycarbonate that has transparency, excellent impact strength and tensile properties, TECANAT GF20 is a 20% glass-reinforced polycarbonate with higher temperature and tensile properties than the unfilled TECANAT.
Polycarbonate is an amorphous thermoplastic. Good electrical properties combined with superior impact strength and moderate chemical resistance make this product widely accepted for numerous applications, This product is offered in many popular rod and plate sizes.
Typical applications include business equipment where gears, rollers, internal mechanical parts, connectors and relays are required. The automotive industry uses polycarbonate materials for pumps, valves, light bezels and instrument panels. It also is applicable to many other industries.
| Главная Информация | |
|---|
| Характеристики | - Хорошая стабильность размеров
- Жесткий, высокий
- Высокая прочность
- Высокая ударопрочность
- Обрабатываемый
- Хорошая электрическая производительность
- Хорошая химическая стойкость
- Высокое разрешение
- Аморфный
|
| Используется | - Детали Насоса
- Шестерня
- Детали клапана/клапана
- Ролик
- Соединитель
- Применение в автомобильной области
- Бизнес-оборудование
|
| Внешний вид | - Прозрачный/прозрачный
- Натуральный цвет
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.19 | g/cm³ | ASTM D792 |
| Поглощение воды 1 | | | ASTM D570 |
| 23°C, 24 hr | 0.15 | % | ASTM D570 |
| Saturated, 23°C | 0.35 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | ASTM D785 |
| M grade, 23°C, injection molding | 70 | | ASTM D785 |
| Grade R, 23°C, Injection Molding | 118 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2340 | MPa | ASTM D638 |
| Прочность на растяжение (Yield, 23°C) | 62.7 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 23°C) | 90 | % | ASTM D638 |
| Флекторный модуль (23°C) | 2210 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 99.3 | MPa | ASTM D790 |
| Коэффициент трения 2(vs. Itself - Dynamic) | 0.38 | | |
| Коэффициент износа 3(0.28 MPa, 0.25 m/sec) | 5000 | 10^-8 mm³/N·m | ASTM D3702 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Незубчатый изод Impact (23°C) | 110 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, unannealed, injection molded | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, injection molded | 132 | °C | ASTM D648 |
| Викат Температура размягчения 4 | 154 | °C | ASTM D1525 |
| CLTE-
Поток 5 | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Удельный нагрев 6 | 1260 | J/kg/°C | ASTM C351 |
| Теплопроводность 7 | 0.19 | W/m/K | ASTM C177 |
| Максимальная температура обслуживания | | | |
| Intermittent | 135 | °C | |
| Long Term | 121 | °C | UL 746B |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости 8 | 1.0E+17 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность 9 | 15 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная | | | ASTM D150 |
| 1 MHz 10 | 2.96 | | ASTM D150 |
| 23°C, 60 Hz 11 | 3.17 | | ASTM D150 |
| Коэффициент рассеивания 12(23°C, 60 Hz) | 9.0E-4 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость 13(1.47 mm) | HB | | UL 94 |
| Дополнительная информация |
|---|
| Data obtained from extruded shapes material unless otherwise noted. |
| Примечание |
|---|
| 1 . | Injection Molded |
| 2 . | 40 psi, 50 fpm; Injection Molded |
| 3 . | Against Steel, Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| 8 . | Injection Molded |
| 9 . | Injection Molded |
| 10 . | Injection Molded |
| 11 . | 50% RH, Injection Molded |
| 12 . | Injection Molded |
| 13 . | Injection Molded |