LUVOCOM® PEEK CLASSIX 7994 VP

Категория	PEEK, Polyetheretherketone
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	0guNBr_LUVOCOM-PEEK-CLASSIX-7994-VP.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®PEEK CLASSIX 7994 VP is a polyetheretherketone (PEEK) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of PEEK CLASSIX 7994 VP are:

Flame Retardant

sterilizable

chemical resistance

Biocompatibility

LUVOCOM®The typical application areas of PEEK CLASSIX 7994 VP are: medical/health care

Главная Информация
Характеристики	Хорошая химическая стойкость Сопротивление гидролизу Биологическая Совместимость Паровая дезинфекция Огнестойкий
Используется	Медицинские принадлежности/принадлежности для ухода
Внешний вид	Красный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.42	g/cm³	ISO 1183
Формовочная усадка	1.0 - 1.6	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.50	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	4500	MPa	ISO 527-2
Tensile Stress (Break)	95.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	4.0	%	ISO 527-2
Флекторный модуль	4000	MPa	ISO 178
Флекторный стресс	145	MPa	ISO 178
Flexural Strain at Flexural Strength	6.0	%	ISO 178

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Ударная прочность (23°C)	5.0	kJ/m²	ISO 179/1eA

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	150	°C	ISO 75-2/A

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+12	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
A	150	°C
B	120	°C
Время сушки
A	3.0 - 6.0	hr
B	6.0 - 8.0	hr
Рекомендуемая максимальная влажность	0.050	%
Задняя температура	360 - 370	°C
Средняя температура	380 - 390	°C
Передняя температура	390 - 400	°C
Температура сопла	360 - 380	°C
Температура обработки (расплава)	390	°C
Температура формы	170 - 190	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Тип материала	Категория	Производитель
LUVOCOM® PEEK CLASSIX 7918	PEEK	Lehmann & Voss & Co.
TECACOMP® PEEK LDS black 3980	PEEK	Ensinger GmbH
RTP 2299 X 115070 F	PEEK	RTP Company
LUVOCOM® 1105-8432	PEEK	Lehmann & Voss & Co.
LUVOCOM® 1105-9193/BL	PEEK	LEHVOSS Group
Plaslube® PEEK CF10 TL10 HF LE	PEEK	Techmer Engineered Solutions