LUVOCOM® 80-8495-2

Категория POM, Acetal (POM) Copolymer
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF 0X2Mb2_LUVOCOM-80-8495-2.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®80-8495-2 is a polyoxymethylene (POM) copolymer material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 80-8495-2 are:
  • flame retardant/rated flame
  • Conductivity
  • Electrostatic protection
  • Good stiffness

Typical application areas include:
  • engineering/industrial accessories
  • textile/fiber
  • Tools
  • Automotive Industry
  • business/office supplies
Главная Информация
Характеристики
  • Проводящий
  • Жесткий, хороший
  • Защита от электростатического разряда
  • Хорошая прочность
Используется
  • Текстильные изделия
  • Неспецифическое применение пищи
  • Инженерные аксессуары
  • Машина/механические детали
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Литьевая форма/инструмент
Внешний вид
  • Синий
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 2.39g/cm³ISO 1183
Плавкий объем-расход (MVR) (190°C/2.16 kg)12.0cm³/10minISO 1133
Формовочная усадка 1.3 - 2.0%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.10%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 5500MPaISO 527-2
Tensile Stress (Break)35.0MPaISO 527-2
Растяжимое напряжение (Yield)2.1%ISO 527-2
Флекторный модуль 4500MPaISO 178
Флекторный стресс 50.0MPaISO 178
Flexural Strain at Flexural Strength 2.6%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 120°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance 1.0E+6ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)12kJ/m²ISO 179/1fU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура непрерывного использования 100°CUL 746B
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Удельное сопротивление поверхности < 1.0E+9ohmsIEC 60093
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость 1HBUL 94
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    A 75.0°C
    Dehumidification desiccant, B 120°C
Время сушки
    A 2.0 - 8.0hr
    Dehumidification desiccant, B 2.0 - 4.0hr
Задняя температура 175 - 190°C
Средняя температура 185 - 205°C
Передняя температура 180 - 200°C
Температура сопла 175 - 200°C
Температура обработки (расплава) 200°C
Температура формы 80.0 - 120°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. When changing from higher melting-point polymers such as polyamides to this product, extremely thorough intermediate cleaning should be carried out. Processing temperatures above 215°C may very rapidly cause thermal damage and should therefore be avoided, particularly as formaldehyde may be eliminated here. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Примечание
1 .Not recognized by UL.
Тип материала Категория Производитель
TYNEA 3902 Acetal (POM) Homopolymer Tyne Plastics LLC.
LNP™ LUBRICOMP™ KP003AXZ compound Acetal (POM) Homopolymer SABIC Innovative Plastics
Kepital® TE-23S Acetal (POM) Copolymer KEP Americas
LNP™ STAT-KON™ KD000 compound Acetal (POM) Copolymer SABIC Innovative Plastics
MAXATEL® AH500AL-NC010 Acetal (POM) Homopolymer Pier One Polymers, Inc.
LNP™ LUBRICOMP™ KAL22 compound Acetal (POM) Copolymer SABIC Innovative Plastics Europe
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами