Описание материалов:
Arlon's AD Series is a group of woven fiberglass-reinforced PTFE composite materials designed for use as printed circuit board substrates. These materials combine the excellent low loss electrical properties of PTFE resin with the enhanced value of costeffective heavier fiberglass styles to provide low cost laminate materials suitable for high volume commercial wireless communication applications.
The AD Series is currently available in a limited combination of dielectric thickness (0.015" - 0.062") and dielectric constant (2.5 - 3.5). Thicker dielectrics can be developed to meet customer requirements. The higher weight ratio of fiberglass to PTFE resin yields laminates with greater dimensional stability than is normally expected of PTFE-based substrates.
Stability of PTFE over a wide frequency range and low loss makes AD Series materials ideal for a variety of microwave and R/F applications in telecom industry. AD Series laminate materials may be processed with standard PTFE materials. Because there is a relatively higher percentage of fiberglass, thermal expansion is reduced in all directions, improving plated through hole reliability.
| Главная Информация | |
|---|
| Наполнитель/армирование | |
| Характеристики | - Цикл быстрого формования
- Хорошая стабильность размеров
|
| Используется | - Компоненты прибора
- Электрическое/электронное применение
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 2.40 | g/cm³ | ASTM D792A |
| Поглощение воды (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ASTM D638 |
| 23°C 1 | 3560 | MPa | |
| 23°C 2 | 4870 | MPa | |
| Флекторный модуль (23°C) | 3720 | MPa | ASTM D790 |
| Компрессионный модуль | 2520 | MPa | ASTM D695 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield | 144 | MPa | |
| TD
: Yield | 119 | MPa | |
| Peel Strength 3 | -2.5 | kN/m | Internal Method |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент линейного теплового расширения | | | |
| X Axis
: 0 to 100°C | 1.2E-5 | cm/cm/°C | Internal Method |
| Y Axis
: 0 to 100°C | 1.5E-5 | cm/cm/°C | Internal Method |
| Z Axis
: 0 to 100°C | 9.5E-5 | cm/cm/°C | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Breakdown Voltage | > 45000 | V | ASTM D149 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Теплопроводность (100°C) | 0.24 | W/m/K | ASTM C177 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 4.5E+7 | ohms | Internal Method |
| Сопротивление громкости | 1.2E+15 | ohms·cm | Internal Method |
| Диэлектрическая постоянная (23°C) | 2.50 | | Internal Method |
| Коэффициент рассеивания (10.0 GHz) | 1.8E-3 | | Internal Method |
| Дуговое сопротивление | > 180 | sec | ASTM D495 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | V-0 | | UL 94 |
| Примечание |
|---|
| 1 . | TD |
| 2 . | MD |
| 3 . | After Thermal Stress |