Описание материалов:
Menzolit® BMC 0400 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor any heavy metals.
Menzolit® BMC 0400 is a low profile DMC/BMC for automotive applications. It fulfils the requirements of the automotive industry regarding painted body panels including reduced C-emissions. For highest surface quality we recommend processing on mirror finish chrome-plated steel moulds. The material shows a high thermal resistance for on-line painting at 190- 200 °C. Adhesion of paint is excellent. The material doesn't shrink during moulding, it even expands. Therefore warpage is reduced and dimensional stability is excellent.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 25% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая адгезия
- Хорошая стабильность размеров
- Без галогенов
- Высокая термостойкость
- Низкая усадка
- Низкий уровень дыма
- Низкий уровень защиты
|
| Используется | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.90 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | -0.050 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 36.0 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, Compression Molded) | 1.0 | % | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 11000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 120 | MPa | ISO 178 |
| Poisson's Ratio | 0.30 | | Internal Method |
| Matrix Crazing Strain | 0.30 | % | Internal Method |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 30 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Температура непрерывного использования | 170 | °C | Internal Method |
| Температура перехода стекла | 170 | °C | DSC |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 160 | °C | |
| Давление впрыска | 2.00 to 8.00 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |